技术性能 | 测试方法 | 公制 |
拉伸强度 | ASTM D638M | 45.7MPa |
断裂伸长率 | ASTM D638M | 7.9% |
屈服伸长率 | ASTM D638M | 3.5% |
弹性模量 | ASTM D638M | 2,460MPa |
泊松比 | ASTM D638M | 0.23 |
弯曲强度 | ASTM D790M | 68.9MPa |
弯曲模量 | ASTM D790M | 2,250MPa |
艾氏耐冲击强度,切口 | ASTM D256A | 23.5J/cm |
硬度 | ASTM D2240 | N/A |
格雷夫斯撕裂 | ASTM D1004 | 123,000N/m |
吸水率 | ASTM D570-98 | 0.24% |
技术性能 | 测试方法 | 公制 |
C.T.E-40℃-0℃ | ASTM E831-00 | 67μm/m-℃ |
C.T.E 0℃-50℃ | ASTM E831-00 | 93μm/m-℃ |
C.T.E 50℃-100℃ | ASTM E831-00 | 156μm/m-℃ |
C.T.E100 ℃-150℃ | ASTM E831-00 | 180μm/m-℃ |
介电常数60Hz | ASTM D150-98 | 3.9-4.1 |
介电常数1Hz | ASTM D150-98 | 3.9 |
介电常数1Hz | ASTM D150-98 | 3.8 |
介电强度1Hz | ASTM D149-97a | 14.6 |
玻璃化温度Tg1Hz | ASTM D1545-00 | 44℃ |
热变形HDT@0.46MPa | ASTM D648-98c | 53℃ |
热变形HDT@1.81MPa | ASTM D648-98c | 48℃ |